SYNTHESIS AND CHARACTERIZATION OF A NEW PHOTOSENSITIVE BENZOFURAN CHALCONE METHACRYLAMIDE MONOMER


İLTER Z., Şenkal B. F., YAKUPHANOĞLU F., AHMEDZADE M.

JOURNAL OF POLYMER ENGINEERING, cilt.28, sa.9, ss.535-551, 2008 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 28 Sayı: 9
  • Basım Tarihi: 2008
  • Dergi Adı: JOURNAL OF POLYMER ENGINEERING
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.535-551
  • İstanbul Teknik Üniversitesi Adresli: Evet

Özet

New methacrylamide monomer, containing pendant benzofuran chalcone moiety, was synthesized by starting from 1-(3-amino-1-benzofuran-2-yl)-3-phenyl prop-2-en-1-one and methacryloyl chloride in the presence of triethyl amine. The polymer was characterized by UV, FT-IR, H-NMR and 13C-NMR spectra and gel permeation chromatography. The photosensitive properties of the polymer were characterized by using UV-visible spectroscopy. In UV-VIS spectra of the polymer, two absorption peaks at 325.67 and 395.95 nm are observed due to pi*pi transition related to >C=C< of the chalcone moieties. The absorption intensity of >C=C< bond is decreased significantly with the irradiation in less than a few minutes at room temperature. The disappearance of the C=C bond in the chalcone moiety suggests that a photo-reaction is taking place in the polymer. This behaviour is very much dependent on the chain length of the chalcone moiety. The thermogravimetric analysis result indicates that the polymer undergoes single thermal state decomposition. The thermal stability temperature of the polymer is 270 degrees C. The glass transition temperature of the polymer was found to be 160 degrees C. This high T-g value of the polymer may be due to the presence of bulky and rigid pendant chalcone units and the short side chains which facilitate chain entanglement.