Modification of the Cu current collector by magnetron sputtering to improve the cycle performance of MxOy (M:Ni,Mn,Co) anodes for lithium ion batteries

Solmaz R., Karahan B. D.

JOURNAL OF ALLOYS AND COMPOUNDS, cilt.872, 2021 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 872
  • Basım Tarihi: 2021
  • Doi Numarası: 10.1016/j.jallcom.2021.159594
  • Dergi Adı: JOURNAL OF ALLOYS AND COMPOUNDS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, PASCAL, Aerospace Database, Chemical Abstracts Core, Communication Abstracts, INSPEC, Metadex, Public Affairs Index, Civil Engineering Abstracts
  • Anahtar Kelimeler: Li ion battery, Ni thin film, Magnetron sputtering, Hydrothermal method, Transition metal oxide anodes, ELECTROCHEMICAL PERFORMANCE, NICO2O4 NANOSHEETS, METAL-OXIDES, NI, COMPOSITE, ELECTRODES, SUPERCAPACITOR, ARRAYS, SHELL, NANOCOMPOSITE
  • İstanbul Teknik Üniversitesi Adresli: Evet

Özet

The present work reports a methodology to produce electrodes with superior performances for batteries. Herein, the fabrication of an anode material that is made of a ternary transition metal oxides (nickel manganese-cobalt containing oxide, NMCO) is achieved by hydrothermal method. Of the two kinds of electrodes prepared, the first is realized by direct lamination of a slurry that contains NMCO powders active materials onto the Cu foil. Then, to improve the mechanical, physical and electrochemical performance of the electrode, a novel design is proposed, where an additional Ni underlay thin film (10 nm thick) is magnetically sputtered onto the Cu foil, before the lamination of NMCO containing slurry (Ni/NMCO). The characterization results show that upon the existence of Ni underlay film both the adhesion as well as the stress accomodation ability of the electrode are improved. Moreover, the charge transfer resistance at the electrode/current collector interface is noted to be decreased due to the presence of the Ni underlay thin film. As a consequence, the galvanostatic tests show that Ni/NMCO anode exhibits an enhanced discharge capacity of 845 mAh g(-1) after 200 cycles under a load of 0.1 A g(-1), whilst the NMCO anode delivers a discharge capacity of 442 mAh g(-1). Moreover, when the Ni/NMCO anode is cycled at 1 A g(-1), it delivers a discharge capacity of 844 mAh g(-1) even after 100 cycles. Considering the position of the magnetron sputtering process in today's industrial applications and its effect on the electrode performance, the results of this study are expected to pave the way for designing electrodes of different battery applications, especially solid state batteries. (c) 2021 Elsevier B.V. All rights reserved.