Titanium diboride synthesis by carbothermal reduction of TiO2 and B2O3

Derin B., Kurtoglu K., Şahin F., Yücel O.

EPD Congress 2008 held at the 2008 Annual TMS Meeting and Exhibition, Louisiana, Amerika Birleşik Devletleri, 9 - 13 Mart 2008, ss.379-383 identifier

  • Yayın Türü: Bildiri / Tam Metin Bildiri
  • Basıldığı Şehir: Louisiana
  • Basıldığı Ülke: Amerika Birleşik Devletleri
  • Sayfa Sayıları: ss.379-383
  • İstanbul Teknik Üniversitesi Adresli: Evet

Özet

The synthesis of titanium diboride (TiB2) by carbothermal reductions of TiO2 and B2O3 was investigated. For this aim, TiO2, B2O3 and carbon black powders were dried, weighed out and mixed in stoichiometric molar proportions (TiO2:B2O3:C = 1:1:5). The experiments were carried out in a graphite resistance furnace in argon media using different range of temperature (1400-1700 degrees C) and time (0 and 15 min). The phase analyses observation of the products were examined by using XRD.