Surface modification of Ti6A14V alloy by pack bonding

Atar E., Kayali E. S., Çimenoğlu H.

TMS 2009 - 138th Annual Meeting and Exhibition, San Francisco, CA, United States Of America, 15 - 19 February 2009, vol.3, pp.601-606 identifier

  • Publication Type: Conference Paper / Full Text
  • Volume: 3
  • City: San Francisco, CA
  • Country: United States Of America
  • Page Numbers: pp.601-606
  • Keywords: Boriding, Surface treatment, Titanium alloy, Wear
  • Istanbul Technical University Affiliated: Yes


In this study, a 10 μm thick uniform boride layer, composed of TiB 2 and TiB phases, was formed on the surface of a Ti6A14V alloy by pack boriding technique. The hardness of the outer most boride layer was 2700 HV0.025· Beneath the boride layer, a boron diffusion zone (BDZ) appeared with a thickness of about 50 μm. The microstructure of the BDZ was composed of randomly oriented TiB whiskers dispersed in the matrix of the base metal. In the BDZ, hardness decreased gradually towards the base metal owing to the reduction of the TiB volume fraction. The borided alloy exhibited excellent wear resistance against Al2O3 ball under both unlubricated and lubricated sliding conditions when compared to the as-received state.